VALOX(沙伯基礎)830/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的 VALOX 830 PBT是一種加30% GR PBT+ PET，表麵光潔度好,典型的應用是熱風槍外殼組件、工業膠槍、電器外殼和把手。
 |
沙伯基礎創新塑料的VALOX 830 PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)830/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 140 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 140 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 10500 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 205 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 205 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7400 | MPa | ASTM D 790 | |
| Taber Abrasion, CS-17, 1 kg | 30 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 140 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 140 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 10500 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 215 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 200 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 8800 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 174 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 123 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 60 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 55 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 800 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 800 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 90 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 90 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 90 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 3 | J | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 50 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 9 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 9 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 10 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 10 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 60 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 50 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 208 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 200 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 208 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 2.7E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 7.8E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 1.97E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.59E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.1E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 1.51E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.42E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 208 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 208 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 220 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 202 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 200 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 120 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 120 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.55 | - | ASTM D 792 | |
| Filler Content | 30 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.4-0.8 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2 mm | 0.2-1 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.6-1 | % | SABIC method | |
| Melt Flow Rate, 265°C/2.16kgf | 16 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 265°C/5.0 kgf | 45 | g/10 min | ASTM D 1238 | |
| Density | 1.55 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.15 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 23 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/2.16 kg | 14 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 35 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 208 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 27 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 23 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 15 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 1 MHz | 3.2 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.013 | - | ASTM D 150 | |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 27 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 23 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 15 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 100 Hz | 3.6 | - | IEC 60250 | |
| Relative Permittivity, 1 MHz | 3.2 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.0008 | - | IEC 60250 | |
| Dissipation Factor, 100 Hz | 0.002 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.013 | - | IEC 60250 | |
| Comparative Tracking Index | 325 | V | IEC 60112 | |
| Comparative Tracking Index, M | 150 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 4 - 6 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 260 - 285 | °C | ||
| Nozzle Temperature | 265 - 275 | °C | ||
| Front - Zone 3 Temperature | 260 - 280 | °C | ||
| Middle - Zone 2 Temperature | 255 - 280 | °C | ||
| Rear - Zone 1 Temperature | 240 - 260 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 60 - 110 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.
熱門文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表參數台化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用於汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：8633 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表參數台化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用於筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：8345 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基於脫模來源於蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：7352 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、複印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：6798 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：6177 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐衝擊，阻燃等級，透明高光澤，適用於電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：5453 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗衝PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助於在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表麵硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：5438 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、複印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：5049 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：5016 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：5005 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用於製造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：4813 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鍾; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：4751 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力於其性能的提高和
瀏覽量：4703 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視遊樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐衝擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐衝擊性之新材料,一般用於計算機外殼及
瀏覽量：4654 -
PC(聚碳酸酯)PC-1100|樂天化學(LOTTE CHEMI···樂天化學的LOTTE Chemical HOPELEX PC PC-1100 是一種聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高強度、FDA/EU 食品容器認證，用於普通注塑產品。 以下是PC(聚碳酸酯)PC-1100/韓國樂天化學
瀏覽量：4533
推薦文章
PBT(聚對苯二甲酸丁二酯)SK612SF|陶氏杜邦/物性表參數陶氏杜邦Crastin PBT SK612SF 是加15%玻璃增強聚對苯二甲酸丁二酯共混物，用於醫療保健行業的，並被廣泛應用於食品接觸領域歐洲和美國在滿足適用的使用條件時。杜邦 Crastin聚對苯二甲酸乙
PPS(聚苯硫醚)A610MG1|TORAY(東麗)物性表參數東麗TORELINA樹脂 PPS A610MG1 是一種GF+MD65增強, 高流動,無機填充物增強的PPS塑膠原材料,東麗均有交聯和線型兩種類PPS, 從基材的聚合到複合工程均有自己的生產線, 為客戶提供多種多樣的產
TPU(熱塑性聚氨酯彈性體)9880DU/科思創/物性表參數科思創(Covestro)的Desmopan(德士模班) TPU 9880DU 是熱塑性聚氨酯彈性體，邵氏硬度76D(DIN ISO 7619-1)，擠出和注射成型等級;具有良好的水解和微生物抗性;很好的低溫衝擊強度，具有抗UV穩定劑
LEONA(尼胺龍)91G55(旭化成)PA66(尼龍66)物性表參數日本旭化成Leona PA66 91G55 是一款加帶壓花玻璃纖維含量為40%高剛性等級尼龍樹脂，典型的特性是抗紫外線性能良好; 良好的強度; 良好剛性; 流動性高; 外觀良好,表麵平滑，低翹曲性，可
ABS(丙烯腈丁二烯苯乙烯)FR15U|沙伯基礎|物性表參數SABIC(沙伯基礎)CYCOLAC ABS FR15U是一種阻燃ABS(丙烯腈丁二烯苯乙烯)，優良的室內紫外線性能，良好的可塑性,UL94V-0/5VA評級,高架UL RTI評級,適於製作一般機械零件,減磨耐磨零件,傳動零件和電訊零件。CYCOLAC FR15U ABS物性表參數PDF文檔下載以下是ABS(丙烯腈丁二烯苯乙烯)FR15U|沙伯基礎|物性表參數物理性能額定值單位製測
PFA(氟聚合物樹脂)440HPB/科慕化學/物性表參數科慕化學Teflon PFA 440HPB X是一種高MFR樹脂的四氟乙烯-全氟烷氧基醚共聚物樹脂，這種氟聚合物樹脂適用於模塑和擠塑應用,熔流率是14MFR（g/10分鍾）(測試條件ASTM D2116),熔點是305℃(581°F)測試條件(ASTM,D4591/D3418),適用於高純度應用中的注塑成型部件(如配件、閥體和過濾器外殼）。以下是PFA(氟聚合物樹脂)440H
XYRON(采龍)L565V|旭化成|PPO(聚苯醚)物性表參數旭化成XYRON PPO L565V 是一種加入50%填料,低翹曲性, 高剛性,高流動阻燃級PPE/PS原料，特點: 良好的耐熱性、尺寸穩定性和機械性能，應用領域: 汽車零件，電氣和電子零件，工業零件，
PC(聚碳酸酯)1803|科思創(Covestro)物性表參數科思創(Covestro)Apec(雅霸)PC 1803是一種高粘度耐高溫聚碳酸酯，比重(23°C)是1.15克/厘米³，熔體流動速率(230°C/2.16kg)是10克/10分鍾，軟化溫度(VST/ b120)=184°C。注射成型熔體溫度在320 - 340°C，應用於刹車燈和指示燈蓋;汽車內飾燈罩;家用燈罩;頭燈鏡片;船燈罩;鹵素係統連接器件。以下是PC(聚碳酸酯)1803|科思
PC(聚碳酸酯)943A|SABIC(沙伯基礎)物性表參數SABIC(沙伯基礎)LEXAN PC(聚碳酸酯)943A是一種抗紫外線，阻燃級別的PC原料，優良外觀、中等粘性，熔流率（熔體流動速率）(300C/1.2 kg)10g/10 min，彎曲強度(屈服50.0 mm 跨距)91.0MPa，懸壁梁缺口
PC(聚碳酸酯)PCG-2105/韓國樂天化學/物性表參數韓國樂天化學的LOTTE Chemical HOPELEX PC PCG-2105 是一種聚碳酸脂塑料(Polycarbonate)，加10%玻璃纖維，厚度1.5 mm防火UL94 V-0 、厚度3.0 mm是防火V-0 、5VA ，特性是普通注塑成型，應用於工業製品。