VALOX(沙伯基礎)815/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的 VALOX 815 PBT是一種加15% GR PBT+ PET，表麵光潔度好,典型的應用是熱風槍外殼組件、工業膠槍、電器外殼和把手。
 |
沙伯基礎創新塑料的VALOX 815 PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)815/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 100 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 100 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 6200 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 155 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 155 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5000 | MPa | ASTM D 790 | |
| Hardness, Rockwell R | 120 | - | ASTM D 785 | |
| Taber Abrasion, CS-17, 1 kg | 17 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 100 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 100 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 6200 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 145 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 4 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 5200 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 102 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 120 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 30 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 30 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 390 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 390 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 60 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 60 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 60 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 6 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 7 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -20°C | 7 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 204 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 210 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 160 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 4.5E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 9.32E-05 | 1/°C | ASTM E 831 | |
| CTE, 60°C to 138°C, flow | 5.4E-05 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.19 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 3.23E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 5.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.41E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.76E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 204 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 210 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 167 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 125 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 110 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.43 | - | ASTM D 792 | |
| Specific Volume | 0.7 | cm³/g | ASTM D 792 | |
| Water Absorption, 24 hours | 0.06 | % | ASTM D 570 | |
| Mold Shrinkage on Tensile Bar, flow | 0.4-0.8 | % | SABIC method | |
| Mold Shrinkage, flow, 1.5-3.2 mm | 0.4-0.6 | % | SABIC method | |
| Mold Shrinkage, flow, 3.2-4.6 mm | 0.6-0.9 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.6-1 | % | SABIC method | |
| Mold Shrinkage, xflow, 1.5-3.2 mm | 0.5-0.8 | % | SABIC method | |
| Mold Shrinkage, xflow, 3.2-4.6 mm | 0.8-1.1 | % | SABIC method | |
| Melt Flow Rate, 250°C/5.0 kgf | 20 | g/10 min | ASTM D 1238 | |
| Melt Flow Rate, 265°C/5.0 kgf | 60 | g/10 min | ASTM D 1238 | |
| Density | 1.43 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.26 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 12 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 50 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 155 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | 5.6E+16 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in air, 3.2 mm | 22 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 23.6 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 100 Hz | 3.6 | - | ASTM D 150 | |
| Relative Permittivity, 1 MHz | 3.5 | - | ASTM D 150 | |
| Dissipation Factor, 100 Hz | 0.002 | - | ASTM D 150 | |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 2 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 2 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, shorttime, 1.0mm | 18 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 100 Hz | 3.6 | - | IEC 60250 | |
| Relative Permittivity, 1 MHz | 2.9 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 100 Hz | 0.002 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 | |
| Comparative Tracking Index | 325 | V | IEC 60112 | |
| Comparative Tracking Index, M | 175 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110-120 | °C | ||
| Drying Time | 4-6 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 260-285 | °C | ||
| Nozzle Temperature | 265-275 | °C | ||
| Front - Zone 3 Temperature | 260-280 | °C | ||
| Middle - Zone 2 Temperature | 255-280 | °C | ||
| Rear - Zone 1 Temperature | 240-260 | °C | ||
| Hopper Temperature | 40-60 | °C | ||
| Mold Temperature | 60-110 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.
熱門文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表參數台化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用於汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：8619 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表參數台化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用於筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：8338 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基於脫模來源於蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：7335 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、複印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：6783 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：6174 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐衝擊，阻燃等級，透明高光澤，適用於電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：5439 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗衝PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助於在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表麵硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：5434 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、複印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：5041 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：5002 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：4991 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用於製造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：4810 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鍾; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：4743 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力於其性能的提高和
瀏覽量：4699 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視遊樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐衝擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐衝擊性之新材料,一般用於計算機外殼及
瀏覽量：4643 -
PC(聚碳酸酯)PC-1100|樂天化學(LOTTE CHEMI···樂天化學的LOTTE Chemical HOPELEX PC PC-1100 是一種聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高強度、FDA/EU 食品容器認證，用於普通注塑產品。 以下是PC(聚碳酸酯)PC-1100/韓國樂天化學
瀏覽量：4527
推薦文章
PP(聚丙烯)PP3684/埃克森美孚(ExxonMobil)物性表參數埃克森美孚(ExxonMobil)Achieve Advanced PP PP3684是一種均聚樹脂設計的紡粘非織造布，熔體流動速率(230°C/2.16kg)是14克/10分鍾，密度(23°C)是0.9克/厘米³，該樹脂特別適合於均勻、高質量織物的出色紡紗，並允許在高紡粘應用中進行創造性的創新，適用於要求低顏色和低氣體褪色變色的應用，用不含故意添加鄰苯二
PPS(聚苯硫醚)A604CX1|TORAY(東麗)物性表參數東麗TORELINA樹脂 PPS A604CX1 是一種GF40%增強, 耐LLC性, 高韌性的PPS塑膠原材料,東麗均有交聯和線型兩種類PPS, 從基材的聚合到複合工程均有自己的生產線, 為客戶提供多種多樣的產品規格。
PC(聚碳酸酯)PCN-2001W/韓國樂天化學/物性表參數韓國樂天化學的LOTTE Chemical HOPELEX PC PCN-2001W 是一種聚碳酸脂塑料(Polycarbonate)，厚度1.5 mm是防火V-2 ，特性是白色普通與防紫外線塑膠原料，應用於工業製品。 以下是PC(聚碳酸酯)PCN-2001W/韓
PA6(尼龍6)BKV25FN04/德國朗盛/物性表參數德國朗盛 LANXESS Durethan PA6 BKV25FN04 是一種加入25%玻璃纖維，注塑，無鹵阻燃，熱老化穩定尼龍6樹脂，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷
TPE(熱塑性彈性體)TC5PAZ/凱柏膠寶/物性表參數凱柏膠寶KRAIBURG TPE TC5PAZ 是一款黑色, 硬度48A,包膠PA材料雙色注塑成型的TPE熱塑性彈性體,典型應用是墊圈、密封件、手柄（手動工具和電動工具等）、撥輪、纜線卡鉤,材料優勢是玻纖量
LEXAN(沙伯基礎)915R/PC(聚碳酸酯)物性表參數沙伯基礎SABIC塑料 LEXAN 915R 聚碳酸酯（PC） 是一種可注射成型的非氯化和非溴化，未填充的阻燃級，具有中/高流動性和良好的釋放性, 它的MVR為18（300C / 1.2kg），UL94 V0@1.1mm，有多種不透
PC（聚碳酸酯）XHT1143|沙伯基礎|物性表參數沙伯基礎PC XHT1143是一種高流動，UV穩定，高耐熱聚碳酸酯共聚物，它是LEXAN XHT組合中紫外線穩定的產品，它有一係列不透明和有限透明的顏色可供選擇，這些數據是由SABIC-IP為亞太地區提供的。以下是PC（聚碳酸酯）XHT1143|沙伯基礎|物性表參數物理性能額定值 (公製)額定值 (英製)測試方法密度1.20 g/cc0.0434
POM(聚甲醛共聚物)GC25A/塞拉尼斯(CELANESE)物性表參數塞拉尼斯(CELANESE)Celcon POM GC25A是一種加25%玻璃纖維增強的聚甲醛共聚物，密度是1.58g/cm³，溶化體積流率（MVR）(190°C/2.16 kg)是10.0cm³/10min，具有優異的強度、剛度和熱變形溫度，模具收縮率低，熱膨脹最小，尺寸穩定性好，可塑性好，適宜做軸承，熱水閥門、精密計量閥、輸送機。以下是POM(聚甲醛共聚物)GC25A/塞
PC(聚碳酸酯)3027U/Samyang(三養)物性表參數Samyang(三養)TRIREX PC3027U是一種非強化,耐氣候聚碳酸酯，比重是1.20g/cm³，熔流率（熔體流動速率）(300°C/1.2 kg)8g/10min，有著優異的機械特性，很好的尺寸穩定性及良好的電氣特性，應用於汽車內飾,汽車外飾,雜貨,電子電器。以下是PC(聚碳酸酯)3027U/Samyang(三養)物性表參數PROPERTYUNITASTM METHODTYPICAL DA
PC(聚碳酸酯)FXD1413T/沙伯基礎/物性表參數Lexan PC FXD1413T 樹脂是清晰的pc -矽氧烷共聚物具有優異的加工性能，在特殊的光擴散顏色。介質流。改進的韌性與中等流量標準PC的顏色相同。顏色包裝可能影響性能。 PC FXD1413T物性表參