PPO(聚苯醚)|NORYL|PX9406P/沙伯基礎/物性表參數

日期：2020-11-06 03:18:23 編輯：科思德塑膠來源：科思德塑膠瀏覽：1395

沙伯基礎(SABIC)NORYL PPO PX9406P是一種阻燃聚苯醚(PPO) ，FR(無鹵化)級樹脂，可能適用於各種電子應用，RTI(impact)= 105°，室外F1等級，以BK黑色顏色為標準。

以下是PPO(聚苯醚)PX9406P/沙伯基礎(NORYL)物性表參數

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
FLAME CHARACTERISTICS	¹⁾
UL Yellow Card Link		E121562-101325734	-	-
UL Yellow Card Link 2		E121562-101325735	-	-
UL Recognized, 94-5VA Flame Class Rating		≥2.5	mm	UL 94
UL Recognized, 94-5VB Flame Class Rating		≥2	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating		≥0.75	mm	UL 94
UL Recognized, 94V-2 Flame Class Rating		≥0.4	mm	UL 94
Glow Wire Ignitability Temperature, 0.75 mm		750	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.0 mm		775	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.5 mm		775	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm		775	°C	IEC 60695-2-13
Glow Wire Flammability Index, 0.75 mm		960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 1.0 mm		960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 1.5 mm		960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 3.0 mm		960	°C	IEC 60695-2-12
UV-light, water exposure/immersion		F1	-	UL 746C
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min		76	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min		55	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min		4.7	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min		9.7	%	ASTM D 638
Tensile Modulus, 50 mm/min		2800	MPa	ASTM D 638
Flexural Stress, yield, 6.4 mm		114	MPa	ASTM D 790
Flexural Stress, yld, 1.3 mm/min, 50 mm span		113	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span		2840	MPa	ASTM D 790
Flexural Modulus, 6.4 mm		2840	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min		73	MPa	ISO 527
Tensile Stress, break, 50 mm/min		55	MPa	ISO 527
Tensile Strain, yield, 50 mm/min		4.5	%	ISO 527
Tensile Strain, break, 50 mm/min		8	%	ISO 527
Tensile Modulus, 1 mm/min		2600	MPa	ISO 527
Flexural Stress, yield, 2 mm/min		110	MPa	ISO 178
Flexural Modulus, 2 mm/min		2500	MPa	ISO 178
IMPACT
Izod Impact, notched, 23°C		140	J/m	ASTM D 256
Izod Impact, notched, -30°C		60	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C		52	J	ASTM D 3763
Izod Impact, notched 80104 +23°C		10	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C		6	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm		11	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80104 sp=62mm		8	kJ/m²	ISO 179/1eA
THERMAL
HDT, 1.82 MPa, 3.2mm, unannealed		118	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed		122	°C	ASTM D 648
Ball Pressure Test, 125°C +/- 2°C		PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate A/120		150	°C	ISO 306
Vicat Softening Temp, Rate B/120		140	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm		117	°C	ISO 75/Af
Relative Temp Index, Elec	¹⁾	110	°C	UL 746B
Relative Temp Index, Mech w/impact	¹⁾	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	¹⁾	110	°C	UL 746B
PHYSICAL
Specific Gravity		1.1	-	ASTM D 792
Melt Volume Rate, MVR at 280°C/5.0 kg		10	cm³/10 min	ISO 1133
ELECTRICAL
Comparative Tracking Index	²⁾	250	V	IEC 60112
Comparative Tracking Index (UL) {PLC}		2	PLC Code	UL 746A
High Amp Arc Ignition (HAI), PLC 0		≥0.75	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 0		≥0.75	mm	UL 746A
High Voltage Arc Track Rate {PLC}		4	PLC Code	UL 746A
Arc Resistance, Tungsten {PLC}		6	PLC Code	ASTM D 495
Injection Molding
Drying Temperature		105-110	°C
Drying Time		3-4	hrs
Drying Time (Cumulative)		8	hrs
Maximum Moisture Content		0.02	%
Melt Temperature		275-305	°C
Nozzle Temperature		275-305	°C
Front - Zone 3 Temperature		265-305	°C
Middle - Zone 2 Temperature		255-300	°C
Rear - Zone 1 Temperature		245-295	°C
Mold Temperature		70-100	°C
Back Pressure		0.3-0.7	MPa
Screw Speed		20-100	rpm
Shot to Cylinder Size		30-70	%
Vent Depth		0.038-0.051	mm