PA66(尼龍66)22G5/長春化工(漳州)/物性表參數
以下是PA66(尼龍66)22G5/長春化工(漳州)/物性表參數
| 密度 | 1.35 g/cc | 0.0488 lb/in³ | |
| 1.49 g/cc | 0.0538 lb/in³ | DAM; ISO 1183 | |
| 吸水率 | 3.4 %
@Thickness 2.00 mm
|
3.4 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 水分吸收 | 0.900 %
@Thickness 2.00 mm
|
0.900 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
| 粘度 | 85370 cP
@Shear Rate 5000 1/s, Temperature 280 °C
|
85370 cP
@Shear Rate 5000 1/s, Temperature 536 °F
|
ISO 11403-1 -2 |
| 138900 cP
@Shear Rate 5000 1/s, Temperature 270 °C
|
138900 cP
@Shear Rate 5000 1/s, Temperature 518 °F
|
ISO 11403-1 -2 | |
| 243400 cP
@Shear Rate 5000 1/s, Temperature 260 °C
|
243400 cP
@Shear Rate 5000 1/s, Temperature 500 °F
|
ISO 11403-1 -2 | |
| 270750 cP
@Shear Rate 500 1/s, Temperature 280 °C
|
270750 cP
@Shear Rate 500 1/s, Temperature 536 °F
|
ISO 11403-1 -2 | |
| 441600 cP
@Shear Rate 500 1/s, Temperature 270 °C
|
441600 cP
@Shear Rate 500 1/s, Temperature 518 °F
|
ISO 11403-1 -2 | |
| 774800 cP
@Shear Rate 500 1/s, Temperature 260 °C
|
774800 cP
@Shear Rate 500 1/s, Temperature 500 °F
|
ISO 11403-1 -2 | |
| 粘度測試 | 140 cm³/g | 140 cm³/g | DAM; ISO 307 1157 1628 |
| 線性成型收縮率,Flow | 0.0020 cm/cm | 0.0020 in/in | DAM; ISO 294-4 2577 |
| 線性成型收縮率，橫向 | 0.010 cm/cm | 0.010 in/in | DAM; ISO 294-4 2577 |
| 機械性能 | 額定值 (公製) | 額定值 (英製) | 測試方法 |
|---|---|---|---|
| 抗張強度(斷裂) | 110 MPa | 16000 psi | 50%RH; ISO 527-1/-2 |
| 125 MPa | 18100 psi | DAM; ISO 527-1/-2 | |
| 抗張強度 | 8.79 MPa
@Strain 0.230 %, Temperature 150 °C
|
1270 psi
@Strain 0.230 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 |
| 12.0 MPa
@Strain 0.240 %, Temperature 90.0 °C
|
1740 psi
@Strain 0.240 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 15.95 MPa
@Strain 0.470 %, Temperature 150 °C
|
2313 psi
@Strain 0.470 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 22.76 MPa
@Strain 0.480 %, Temperature 90.0 °C
|
3301 psi
@Strain 0.480 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 24.06 MPa
@Strain 0.700 %, Temperature 150 °C
|
3490 psi
@Strain 0.700 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 25.92 MPa
@Strain 0.400 %, Temperature 40.0 °C
|
3759 psi
@Strain 0.400 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 31.12 MPa
@Strain 1.10 %, Temperature 150 °C
|
4514 psi
@Strain 1.10 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 34.25 MPa
@Strain 0.790 %, Temperature 90.0 °C
|
4968 psi
@Strain 0.790 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 37.13 MPa
@Strain 0.540 %, Temperature 40.0 °C
|
5385 psi
@Strain 0.540 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 41.37 MPa
@Strain 0.570 %, Temperature 23.0 °C
|
6000 psi
@Strain 0.570 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 41.5 MPa
@Strain 0.470 %, Temperature 23.0 °C
|
6020 psi
@Strain 0.470 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 42.25 MPa
@Strain 1.55 %, Temperature 150 °C
|
6128 psi
@Strain 1.55 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 44.11 MPa
@Strain 2.01 %, Temperature 150 °C
|
6398 psi
@Strain 2.01 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 44.88 MPa
@Strain 1.15 %, Temperature 90.0 °C
|
6509 psi
@Strain 1.15 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 52.61 MPa
@Strain 3.26 %, Temperature 150 °C
|
7630 psi
@Strain 3.26 %, Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 54.28 MPa
@Strain 0.980 %, Temperature 40.0 °C
|
7873 psi
@Strain 0.980 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 55.02 MPa
@Strain 2.75 %, Temperature 150 °C
|
7980 psi
@Strain 2.75 %, Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 57.51 MPa
@Strain 1.63 %, Temperature 90.0 °C
|
8341 psi
@Strain 1.63 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 63.12 MPa
@Strain 2.08 %, Temperature 90.0 °C
|
9155 psi
@Strain 2.08 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 63.72 MPa
@Strain 0.650 %, Temperature -20.0 °C
|
9242 psi
@Strain 0.650 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 67.98 MPa
@Strain 0.820 %, Temperature 0.000 °C
|
9860 psi
@Strain 0.820 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 71.93 MPa
@Strain 3.50 %, Temperature 90.0 °C
|
10430 psi
@Strain 3.50 %, Temperature 194 °F
|
50%RH; ISO 11403-1 -2 | |
| 72.3 MPa
@Strain 0.770 %, Temperature 0.000 °C
|
10500 psi
@Strain 0.770 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 73.4 MPa
@Strain 1.26 %, Temperature 40.0 °C
|
10600 psi
@Strain 1.26 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 73.91 MPa
@Strain 1.18 %, Temperature 23.0 °C
|
10720 psi
@Strain 1.18 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 74.49 MPa
@Strain 2.80 %, Temperature 90.0 °C
|
10800 psi
@Strain 2.80 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
| 78.89 MPa
@Strain 0.830 %, Temperature -20.0 °C
|
11440 psi
@Strain 0.830 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 79.11 MPa
@Strain 1.75 %, Temperature 40.0 °C
|
11470 psi
@Strain 1.75 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 84.04 MPa
@Strain 1.04 %, Temperature 23.0 °C
|
12190 psi
@Strain 1.04 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 94.42 MPa
@Strain 2.82 %, Temperature 40.0 °C
|
13690 psi
@Strain 2.82 %, Temperature 104 °F
|
50%RH; ISO 11403-1 -2 | |
| 100.33 MPa
@Strain 1.96 %, Temperature 23.0 °C
|
14552 psi
@Strain 1.96 %, Temperature 73.4 °F
|
50%RH; ISO 11403-1 -2 | |
| 100.68 MPa
@Strain 1.34 %, Temperature 0.000 °C
|
14602 psi
@Strain 1.34 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 100.92 MPa
@Strain 2.18 %, Temperature 40.0 °C
|
14637 psi
@Strain 2.18 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
| 101.62 MPa
@Strain 1.11 %, Temperature -20.0 °C
|
14739 psi
@Strain 1.11 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 118.66 MPa
@Strain 1.78 %, Temperature 23.0 °C
|
17210 psi
@Strain 1.78 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
| 120.54 MPa
@Strain 1.46 %, Temperature 0.000 °C
|
17483 psi
@Strain 1.46 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 127.28 MPa
@Strain 1.98 %, Temperature 0.000 °C
|
18460 psi
@Strain 1.98 %, Temperature 32.0 °F
|
50%RH; ISO 11403-1 -2 | |
| 134.63 MPa
@Strain 1.66 %, Temperature -20.0 °C
|
19526 psi
@Strain 1.66 %, Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 142.85 MPa
@Strain 1.74 %, Temperature -20.0 °C
|
20719 psi
@Strain 1.74 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 157.09 MPa
@Strain 2.33 %, Temperature 0.000 °C
|
22784 psi
@Strain 2.33 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
| 伸長率 (斷裂) | 2.0 % | 2.0 % | DAM; ISO 527-1/-2 |
| 2.6 % | 2.6 % | 50%RH; ISO 527-1/-2 | |
| 拉伸模量 | 7.50 GPa | 1090 ksi | 50%RH; ISO 527-1/-2 |
| 9.00 GPa | 1310 ksi | DAM; ISO 527-1/-2 | |
| 3.213 GPa
@Temperature 150 °C
|
466.0 ksi
@Temperature 302 °F
|
50%RH; ISO 11403-1 -2 | |
| 3.595 GPa
@Temperature 150 °C
|
521.4 ksi
@Temperature 302 °F
|
DAM; ISO 11403-1 -2 | |
| 5.515 GPa
@Temperature 60.0 °C
|
799.9 ksi
@Temperature 140 °F
|
50%RH; ISO 11403-1 -2 | |
| 5.62 GPa
@Temperature 60.0 °C
|
815 ksi
@Temperature 140 °F
|
DAM; ISO 11403-1 -2 | |
| 10.386 GPa
@Temperature -20.0 °C
|
1506.4 ksi
@Temperature -4.00 °F
|
50%RH; ISO 11403-1 -2 | |
| 10.498 GPa
@Temperature -20.0 °C
|
1522.6 ksi
@Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
| 割線模量 | 4.16 GPa
@Strain 2.06 %, Temperature 40.0 °C
|
603 ksi
@Strain 2.06 %, Temperature 104 °F
|
 |
PA66(尼龍66)22G5/長春化工(漳州)/物性表參數 |
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.
熱門文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表參數台化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用於汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：8633 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表參數台化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用於筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：8345 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基於脫模來源於蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：7352 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、複印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：6797 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：6176 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐衝擊，阻燃等級，透明高光澤，適用於電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：5453 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗衝PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助於在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表麵硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：5438 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、複印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：5049 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：5016 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：5005 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用於製造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：4813 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鍾; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：4750 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力於其性能的提高和
瀏覽量：4703 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視遊樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐衝擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐衝擊性之新材料,一般用於計算機外殼及
瀏覽量：4654 -
PC(聚碳酸酯)PC-1100|樂天化學(LOTTE CHEMI···樂天化學的LOTTE Chemical HOPELEX PC PC-1100 是一種聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高強度、FDA/EU 食品容器認證，用於普通注塑產品。 以下是PC(聚碳酸酯)PC-1100/韓國樂天化學
瀏覽量：4533
推薦文章
PBT(聚對苯二甲酸丁二酯)B2520|巴斯夫|物性表參數巴斯夫ULTRADUR PBT B2520 是一款未增強PBT原材料,良好的流動性、耐水解性，用於連接器、汽車領域，Ultradur是巴斯夫公司部分晶體飽和聚酯產品係列的商標名稱，該生產線以聚（丁烯
- Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金)物性表參數
科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
TPE(熱塑性彈性體)OC7OAZ/凱柏膠寶/物性表參數凱柏膠寶KRAIBURG尼塑寶 TPE OC7OAZ 是一款耐化學TPE,硬度是69A黑色TPE材料,AD/PAX/CR係列是用於電子應用中的雙組件密封和機器工具中軟質把手和手柄的材料解決方案。該材料擁有卓越的耐護膚
TPU(熱塑性聚氨酯彈性體)6088AU/科思創/物性表參數科思創(Covestro)的Desmopan(德士模班) TPU 6088AU 是熱塑性聚氨酯彈性體，邵氏硬度88A(DIN ISO 7619-1)，注塑級，具有良好的水解和微生物抗性;簡單的流動;具有特殊的UV穩定劑;性能是低磨損, 耐氣
ForTii(荷蘭帝斯曼)F11C/PA4T(尼龍4T)物性表參數荷蘭帝斯曼ForTii F11C PA4T 是一種30% 玻纖增強, 阻燃劑, 不含鹵素和紅磷, 顏色穩定性改良的尼龍4T材料,ForTii突破性的高溫聚酰胺，無鹵阻燃牌號可用於電子、照明、汽車、白色家電、航空
Pebax(尼龍彈性體)5533 SA 01|阿科瑪(ARKEMA)物性表參數阿科瑪(ARKEMA)聚醚嵌段酰胺Pebax 5533 SA 01樹脂是一種由柔性聚醚和硬質聚酰胺聚合的熱塑性塑料彈性體，該SA牌號專用於食品應用。以下是Pebax(尼龍彈性體)5533 SA 01|阿科瑪(ARKEMA)物性表參數 基本信息特性脫模性能良好用途非特定食品應用/管件形式粒子加工方法擠出/注射成型物理性能額定值單位製測試方法密度 1.01g/cm³
PBT(聚對苯二甲酸丁二酯)SEF-530X|三菱塑料|物性表參數三菱工程塑料NOVADURAN PBT SEF-530X是一種聚對苯二甲酸丁二酯(PBT)材料，熔融體積流量（MVR)(cm³/10min)是17((250°C/5.0kg))，簡支梁缺口衝擊強度(kJ/m²)是7.0(23°C)，UL阻燃等級是V-0(0.75mm)，含有的填充物為30%玻璃纖維增強材料，加工方式為：注射成型，NOVADURAN SEF-530X主要特性為:阻燃/額定火焰。以下是PBT
PC（聚碳酸酯）XHT3141|沙伯基礎|物性表參數沙伯基礎PC XHT3141是一種高流動、高耐熱的聚碳酸酯共聚物，它有一係列不透明和有限透明的顏色可供選擇。以下是PC（聚碳酸酯）XHT3141|沙伯基礎|物性表參數物理性能額定值單位製測試方法比重 1.20g/cm³ASTM D792, ISO 1183熔流率（熔體流動速率） (330°C/2.16 kg)33g/10 minASTM D1238溶化體積流率（MVR） (330°C/2.16 k
PBT(熱塑性聚酯)B4300G3|巴斯夫|物性表參數巴斯夫ULTRADUR PBT B4300G3 是一款易於流動的注塑PBT，采用15%的玻璃纖維加固，適用於剛性、韌性和尺寸穩定的零件,典型的應用包括計時器刻度盤、開關、旋鈕、恒溫器部件、烤箱門把
PA46(尼龍46)TW241F8|恩驊力(Envalior)物性表參數恩驊力(Envalior)(原帝斯曼DSM)Stanyl聚合物PA46 TW241F8是一款加40%玻纖增強, 熱穩定,注塑成型的PA46原料，應用於EPS轉向組件、齒輪、撓性聯軸器和傳感器、EPS齒輪、油泵齒輪（汽車），Stanyl作為高性能聚酰胺,在對耐熱性、設計硬度、摩擦磨耗以及流動性都有要求的嚴苛的應用中表現優異，Stanyl能在高達220℃時依舊保持良好