VALOX(沙伯基礎)HX312C/PBT熱塑性聚酯/物性表參數

日期：2020-04-20 01:30:32 編輯：科思德塑膠來源：科思德塑膠瀏覽：410

沙伯基礎創新塑料SABIC的 VALOX HX312C PBT是一種無加強PBT,用於醫療器械和醫藥應用,醫療保健管理的變化，生物兼容(ISO 10993或USP類VI)，食品接觸合規,電子煙和蒸汽可消毒。

以下是VALOX(沙伯基礎)HX312C/PBT熱塑性聚酯/物性表參數

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min	51	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	30	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	25	%	ASTM D 638
Tensile Modulus, 50 mm/min	2500	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	82	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2340	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	58	MPa	ISO 527
Tensile Stress, break, 50 mm/min	30	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6	%	ISO 527
Tensile Strain, break, 50 mm/min	25	%	ISO 527
Tensile Modulus, 1 mm/min	2500	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	85	MPa	ISO 178
Flexural Modulus, 2 mm/min	2400	MPa	ISO 178
IMPACT
Izod Impact, notched, 23°C	53	J/m	ASTM D 256
Izod Impact, notched, -30°C	53	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	40	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	NB	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80104 -30°C	NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	3	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	3	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	3	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80104 sp=62mm	2	kJ/m²	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80104 sp=62mm	NB	kJ/m²	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80104 sp=62mm	NB	kJ/m²	ISO 179/1eU
THERMAL
Vicat Softening Temp, Rate B/50	175	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed	54	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.E-04	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	1.E-04	1/°C	ASTM E 831
CTE, 23°C to 80°C, flow	1.E-04	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	1.E-04	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	175	°C	ISO 306
Vicat Softening Temp, Rate B/120	165	°C	ISO 306
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	58	°C	ISO 75/Ae
PHYSICAL
Specific Gravity	1.31	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.9-1.6	%	SABIC method
Melt Flow Rate, 250°C/1.2 kgf	35	g/10 min	ASTM D 1238
Density	1.31	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.35	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.08	%	ISO 62
Melt Volume Rate, MVR at 250°C/1.2 kg	31	cm³/10 min	ISO 1133
Injection Molding
Drying Temperature	110-120	°C
Drying Time	2-4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250-270	°C
Nozzle Temperature	240-260	°C
Front - Zone 3 Temperature	245-265	°C
Middle - Zone 2 Temperature	240-255	°C
Rear - Zone 1 Temperature	230-245	°C
Hopper Temperature	40-60	°C
Mold Temperature	40-100	°C

溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.

上一頁：VALOX(沙伯基礎)HX3091HP/PBT熱塑性聚酯/物性表參數下一頁：VALOX(沙伯基礎)HX420HP/PBT熱塑性聚酯/物性表參數

返回首頁返回物性參數列表

VALOX(沙伯基礎)HX312C/PBT熱塑性聚酯/物性表參數

熱門文章

推薦文章