VALOX(沙伯基礎)735/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的 VALOX 735 PBT是一種加40%玻璃/礦物，優異的熱工性能/低收縮,電動加熱設備，適配器環，烤箱烤架等,提供黑色/自然色。
 |
沙伯基礎創新塑料的VALOX 735 PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)735/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 95 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 95 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 2 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 10400 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8300 | MPa | ASTM D 790 | |
| Taber Abrasion, CS-17, 1 kg | 64 | mg/1000cy | SABIC method | |
| Tensile Stress, yield, 5 mm/min | 90 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 90 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 10000 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 130 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 130 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 2 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 8300 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 144 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 124 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 40 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 30 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 560 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 520 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 60 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 55 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 50 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 5 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 7 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 7 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 185 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 215 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 190 | °C | ASTM D 648 | |
| Thermal Conductivity | 0.36 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 2.28E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.53E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 2.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 2.18E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.4E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 180 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 180 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 190 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.62 | - | ASTM D 792 | |
| Filler Content | 40 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.6 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-0.8 | % | SABIC method | |
| Melt Flow Rate, 266°C/5.0 kgf | 20 | g/10 min | ASTM D 1238 | |
| Density | 1.62 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.96 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 1 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 3 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 15 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 160 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 45 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 22 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D 149 | |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 45 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 22 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.008 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.017 | - | IEC 60250 | |
| Relative Permittivity, 50/60 Hz | 3.5 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 0.81 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 4 - 6 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 260 - 285 | °C | ||
| Nozzle Temperature | 265 - 275 | °C | ||
| Front - Zone 3 Temperature | 260 - 280 | °C | ||
| Middle - Zone 2 Temperature | 255 - 280 | °C | ||
| Rear - Zone 1 Temperature | 240 - 260 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 60 - 110 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.
熱門文章
-
PC/ABS(PC+ABS合金)AC2300/台化/物性表參數台化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用於汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：8615 -
PC/ABS(PC+ABS合金)AC3100/台化/物性表參數台化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用於筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：8331 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基於脫模來源於蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：7313 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、複印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：6773 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：6169 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗衝PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助於在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表麵硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：5433 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐衝擊，阻燃等級，透明高光澤，適用於電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：5430 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、複印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：5023 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：4986 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：4981 -
COC(環烯烴共聚物)E48R|ZEONEX(瑞翁)物性表···瑞翁ZEONEX COC E48R 是一種烯烴聚合物(COP)具有優異的光學性能，可用於製造相機和激光打印機的光學部件，比重是1.01g/cm(ASTM D792)，熔流率（熔體流動速率）(280C/2.16 kg)是25g/10 min，ZEO
瀏覽量：4801 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鍾; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：4736 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力於其性能的提高和
瀏覽量：4695 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視遊樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐衝擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐衝擊性之新材料,一般用於計算機外殼及
瀏覽量：4639 -
PC(聚碳酸酯)PC-1100|樂天化學(LOTTE CHEMI···樂天化學的LOTTE Chemical HOPELEX PC PC-1100 是一種聚碳酸脂塑料(Polycarbonate)，特性是中等粘度、高強度、FDA/EU 食品容器認證，用於普通注塑產品。 以下是PC(聚碳酸酯)PC-1100/韓國樂天化學
瀏覽量：4521
推薦文章
LCP/E440I/LCP物性表參數LCP E440I 物性表參數 Celanese VECTRA E440i ( 液晶聚合物 -LCP 塑料 ) 本物性表由 www.cn-plas.com 塑料網提供，轉載請注明來源！ Physical Properties 物理性質 Metric 公製數據 English 英製數據 Comments 測試
POM(聚甲醛樹脂)GH-25D/日本寶理/物性表參數日本寶理奪鋼DURACON POM GH-25D 是一種加玻纖25%,高流動性,玻璃纖維增強聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器
PA6(尼龍6)B2730G/神馬華威(Shenma Warwick)物性表參數神馬華威(Shenma Warwick)PA6 B2730G是一種加30%玻璃纖維增強尼龍6材料，性能是易成型，通常用於製造各種類型的管道、管件、輸送帶和製動器等。以下是PA6(尼龍6)B2730G/神馬華威(Shenma Warwick)物性表參數產品特性易成型填充增強增強填充30% 玻纖技術參數物理性能值/單位測試標準測試條件密度1.36 g/cm³ISO 118323℃
TPV(熱塑性硫化橡膠)271-64/塞拉尼斯/物性表參數塞拉尼斯Santoprene TPV 271-64是一種硬度69A的TPV(熱塑性硫化彈性體)，比重是0.970g/cm，耐連續高溫度 (1008 hr)135C，這種熱塑性彈性體(TPV)家族中的一種柔軟、可著色的特種熱塑性硫化膠(TPV)，它是設計用於非脂肪食品接觸應用，該等級的Santoprene TPV是剪切依賴的，可以在傳統的熱塑性塑料設備上進行注射成型，擠出或吹
ABS(丙烯腈-丁二烯-苯乙烯共聚物)HF380I|LG化學|物性表參數LG化學的ABS HF380I是一種可噴塗的丙烯腈-丁二烯-苯乙烯共聚物，熔體流動速率(230°C/2.16kg)是40克/10分鍾，比重(23°C)是1.05克/厘米³，應用於電氣/電子應用領域。以下是ABS(丙烯腈-丁二烯-苯乙烯共聚物)HF380I|LG化學|物性表參數基本信息黃卡編號E67171-248362特性可噴塗的、流動性高用途汽車領域的應用加工方法注射成型
- PA66(尼龍66)27F-303/神馬華威(Shenma Warwick)物性表參數
神馬華威(Shenma Warwick)PA66 27F-303是一種阻燃尼龍66材料，性能是易成型，通常用於製造各種類型的工業用品、化工用品和電子產品等。以下是PA66(尼龍66)27F-303/神馬華威(Shenma Warwick)物性表參數產品特性阻燃顏色形狀粒狀白色技術參數物理性能值/單位測試標準測試條件密度1.19 g/cm³ISO 118323℃, Dry吸水率2 %
PP(聚丙烯)RP344NK/利安德巴塞爾/物性表參數利安德巴塞爾(Lyondellbasell)Moplen PP RP344NK是一種成核聚丙烯無規共聚物，熔體流動速率(230°C/2.16kg)是13克/10分鍾，密度(23°C)是0.9克/厘米³，具有良好的可加工性，低加工溫度下具有優異的透明度，生產率高，氣孔形成少，力學性能平衡好，典型的客戶應用是用於食品和非食品的透明容器、家庭用品、瓶子(IBM/ISBM)
PC/PET(PC+PET合金)HX7509HP|沙伯基礎|物性表參數沙伯基礎(SABIC)XYLEX HX7509HP PC/PET是一種中分子聚碳酸酯/聚酯合金;包含脫模，用於醫療器械和醫用，保健管理的變化，生物兼容(iso10993或USP類VI)，食品接觸兼容。XYLEX HX7509HP PC/PET物性表參數PDF文檔下載以下是沙伯基礎創新塑料XYLEX HX7509HP PC/PET物性表參數物理性能額定值單位製測試方法比重 1.20g/cm³ASTM D7
PPA(聚鄰苯二甲酰胺)A-8950HS|SOLVAY(索爾維)物性表參數索爾維(SOLVAY) AMODEL A-8950HS PPA 是一種加50%玻璃增強等級的PPA材料，熱穩定具有高熱撓度溫度和非常高的拉伸強度,該樹脂還具有優異的抗蠕變性、低吸濕性和抗油性。-黑色:A-8950 HS
PC（聚碳酸酯）EX1332T|沙伯基礎|物性表參數沙伯基礎LEXAN PC EX1332T是聚碳酸酯樹脂，MVR (300C/1.2kg) 2 cm3/10min，高粘度，支化，擠壓，脫模，UV穩定，透明，半透明和不透明的顏色。以下是PC（聚碳酸酯）EX1332T/沙伯基礎/物性表參數物理性能額定值單位製測試方法密度 1.20g/cm³ISO 1183溶化體積流率（MVR） ISO 1133300°C/1.2 kg3.00c