VALOX(沙伯基礎)4031/PBT熱塑性聚酯/物性表參數
沙伯基礎創新塑料SABIC的VALOX 4031 PBT是一種加30%高強度玻璃纖維增強PBT注塑樹脂，具有優異的強度、剛度和耐熱性,用途:電器手柄、射燈、電機。
 |
沙伯基礎創新塑料的VALOX 4031 PBT物性表參數PDF文檔下載 |
以下是VALOX(沙伯基礎)4031/PBT熱塑性聚酯/物性表參數
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 140 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 140 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 10000 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D 790 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 190 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7900 | MPa | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 135 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 135 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 10000 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 210 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 200 | MPa | ISO 178 | |
| Flexural Strain, break, 2 mm/min | 3 | % | ISO 178 | |
| Flexural Modulus, 2 mm/min | 8300 | MPa | ISO 178 | |
| Ball Indentation Hardness, H358/30 | 125 | MPa | ISO 2039-1 | |
| Hardness, Rockwell R | 125 | - | ISO 2039-2 | |
| IMPACT | ||||
| Charpy Impact, unnotched, 23°C | 65 | kJ/m² | ISO 179/2C | |
| Charpy Impact, unnotched, -30°C | 60 | kJ/m² | ISO 179/2C | |
| Izod Impact, unnotched, 23°C | 880 | J/m | ASTM D 4812 | |
| Izod Impact, unnotched, -30°C | 880 | J/m | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 100 | J/m | ASTM D 256 | |
| Izod Impact, notched, 0°C | 100 | J/m | ASTM D 256 | |
| Izod Impact, notched, -30°C | 100 | J/m | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 55 | kJ/m² | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 55 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 0°C | 11 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, 23°C | 12 | kJ/m² | ISO 179/2C | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA | |
| Charpy Impact, notched, -30°C | 12 | kJ/m² | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 50 | kJ/m² | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 55 | kJ/m² | ISO 179/1eU | |
| THERMAL | ||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 220 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 2.1E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, flow | 3.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, flow | 1.98E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 150°C, xflow | 1.73E-04 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 215 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 220 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Ae | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 205 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 140 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 140 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.54 | - | ASTM D 792 | |
| Filler Content | 30 | % | ASTM D 229 | |
| Mold Shrinkage on Tensile Bar, flow | 0.3-0.7 | % | SABIC method | |
| Mold Shrinkage on Tensile Bar, xflow | 0.5-1 | % | SABIC method | |
| Melt Flow Rate, 266°C/5.0 kgf | 50 | g/10 min | ASTM D 1238 | |
| Density | 1.54 | g/cm³ | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.26 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 | |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 12 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 30 | cm³/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 40 | cm³/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 | 150 | Pa-s | ISO 11443 | |
| ELECTRICAL | ||||
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | ASTM D 149 | |
| Dielectric Strength, in oil, 3.2 mm | 18 | kV/mm | ASTM D 149 | |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 1 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 26 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 15 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 3.1 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.0016 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | ||||
| UL Recognized, 94HB Flame Class Rating | 0.84 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value | 6 | mm | UL 94 | |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Injection Molding | ||||
| Drying Temperature | 110 - 120 | °C | ||
| Drying Time | 2 - 4 | hrs | ||
| Maximum Moisture Content | 0.02 | % | ||
| Melt Temperature | 250 - 270 | °C | ||
| Nozzle Temperature | 240 - 260 | °C | ||
| Front - Zone 3 Temperature | 245 - 265 | °C | ||
| Middle - Zone 2 Temperature | 240 - 255 | °C | ||
| Rear - Zone 1 Temperature | 230 - 245 | °C | ||
| Hopper Temperature | 40 - 60 | °C | ||
| Mold Temperature | 40 - 100 | °C |
溫馨提示：
本物性表參數提供者不承擔任何法律責任，建議在選擇材料前，就數據值與塑膠材料廠商進行驗證。版權歸原作者所有，如有侵權請立即與我們聯係.
熱門文章
-
PC/ABS(PC+ABS合金)AC3100/台化/物性表參數台化TAIRILOY PC/ABS AC3100是無氯、無溴、無銻阻燃級合金樹脂，應用於筆記型電腦外殼、光碟機Loader及 Tray盤、螢幕外殼、數位相機外殼、事務機器外殼、家用電器外殼、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性
瀏覽量：13348 -
PC/ABS(PC+ABS合金)AC2300/台化/物性表參數台化TAIRILOY PC/ABS AC2300是電鍍級合金樹脂，應用於汽車門把、儀表板、輪圈蓋、汽車零件、消費性電子元件，TAIRILOY PC/ABS合膠具有ABS的加工性及耐低溫機械性能，亦同時具有PC的高衝擊性及耐熱性特質，可應用於汽車零件、3C電子產品外殼、消費性電子元件、家電外殼、玩具、板材等產品上，其應用端多元化，本廠設有
瀏覽量：11506 -
TRITAN(美國伊士曼)TX1001/PCTG(共聚聚酯)物···美國伊士曼TRITAN PCTG TX1001 是一種無定形共聚酯，具有極好的外觀和清晰度,EastmanTritanTX1001包含一個基於脫模來源於蔬菜來源。其最突出的特點是優良的韌性、水解穩定性、耐熱性和耐化
瀏覽量：11080 -
ABS塑料樹脂/PA-757/奇美實業/物性表參數奇美實業POLYLAC ABS PA-757 是一般級高光澤性、超高剛性、特佳彎曲強度的ABS樹脂,熔融指數是22.g/10min,用途是電視機前殼、複印機外殼 、電話機殼 、化妝品盒 、輪胎蓋,奇美的POLYLACABS樹脂
瀏覽量：9317 -
PC(聚碳酸酯)FR6005/科思創(Makrolon)物性表···科思創(Covestro)模克隆(Makrolon) PC FR6005 是聚碳酸酯全球品級; 體積熔融指數MVR(300℃/1.2 kg) 9.0cm cm /10 min，中粘度，耐衝擊，阻燃等級，透明高光澤，適用於電子/電氣產品。 以下是PC(聚碳酸
瀏覽量：8126 -
PLA(聚乳酸)4032D|NatureWorks(Ingeo)物性表···Nature Works聚乳酸Ingeo PLA 4032D是轉換成雙軸取向的薄膜，使用溫度高達300°F(150°C)，該薄膜具有優良的光學性能、良好的可加工性和優良的扭折性，這些特性使4032D薄膜成為層壓和其他包裝應用的理想產品，其他性能包括阻隔風味、油脂和耐油性。Nature Works Ingeo PLA 4032D物性表參數PDF文檔下載以下是PLA(聚乳酸)4032
瀏覽量：8114 -
PA66(尼龍66)CM3006G-30|TORAY(東麗)物性表···TORAY(東麗)Nylon樹脂AMILAN PA66 CM3006G-30 是一種加30%玻纖增強，耐熱級別的尼龍66原料，拉伸強度在23℃測試條件是190MPa,更是一種含有酰胺基(-CONH-)的熱塑性工程塑料，此外還為客戶的各種需
瀏覽量：7538 -
POM(聚甲醛樹脂)M90-44/寶理塑料/物性表參數···寶理塑料(奪鋼)DURACON POM M90-44是一種標準全球品級型號,高流動性聚甲醛,奪鋼就是這種共聚物的典型代表；主要以在齒輪、螺絲及軸承等機械零件方麵的應用為中心。應用在DVD播放器、Blu-ray 光盤播放器等AV機器；打印機、複印機等OA機器；洗衣機、冰箱、剃須刀等家用電器；油箱蓋、燃料油泵、安全帶零部件以及汽車內飾用品等
瀏覽量：6974 -
Bayblend(拜本蘭)FR3010|科思創(PC/ABS合金···科思創Bayblend PC/ABS FR3010 是加阻燃,劑維卡軟化點溫度/ B 120 = 110C;耐熱性增加;UL認可94 V-0為1.5 mm;灼熱絲溫度(GWFI):在2.0毫米960C;改進的化學抗性和應力開裂行為;繼任者FR2010. PC/ABS是聚碳酸
瀏覽量：6820 -
PA12(尼龍12)TR90|瑞士EMS化學|物性表參數科思德塑膠網站提供瑞士EMS化學PA12 TR90的物性表參數下載，並且有Grilamid PA12 TR90塑膠粒銷售，為您提供詳細的瑞士EMS化學PA12(尼龍12)TR90資料以及報價。
瀏覽量：6643 -
PP(聚丙烯)HJ730|韓華道達爾(Hanwha)物性表···韓華道達爾(Hanwha)高抗衝PP HJ730是與普通均聚PP相比具有高等規高結晶度的特點，這一產品的結晶性能使其具有更好的強度和耐熱性。HJ730非常有助於在電子電器產品和高強度汽車部件上使用，這些部件需要在高溫環境下長期暴露.其特點是：高強度、超高耐熱、高結晶度、良好的表麵硬度、良好的色粉分散性。韓華道達爾PP HJ730物
瀏覽量：6598 -
Makrolon(模克隆)2407(科思創)PC(聚碳酸酯)···科思創Makrolon 2407 PC材料介紹： Makrolon 2407 PC是全球品級; 體積熔融指數19 厘米 3 /10分鍾; 普通用途; 紫外線穩定; 易脫模; 注塑成型; 可提供透明, 半透明和不透明顏色. Makrolon 2407物性表P
瀏覽量：6456 -
PC/ABS(PC+ABS合金)PC-540|奇美實業|物性表···奇美實業WONDERLOY PC/ABS PC-540是防火級不含鹵素的難燃PC合金樹脂,熔融指數是22.g/10min,用途是機頂盒、投影機、顯示器前框、3C數碼產品、變壓器、電視遊樂器、小平板計算機、網通產品,為了增加PC在薄肉產品的耐衝擊性，可加入ABS樹脂進行摻合(blending)，可形成同時具有高剛性及高耐衝擊性之新材料,一般用於計算機外殼及
瀏覽量：6320 -
TRITAN(美國伊士曼)TX1501HF/PCTG(共聚聚酯···美國伊士曼TRITAN PCTG TX1501HF 是一種伊士曼TRITAN的高流動級材料，TRITAN共聚酯TX1501HF粘度降低40 - 50%的相對於伊士曼TRITAN共聚酯TX1001，其他突出的特點包括良好的韌性，水解穩定性，耐熱性
瀏覽量：6295 -
PC(聚碳酸酯)L-1250Y|嘉興帝人|物性表參數嘉興帝人Panlite PC L-1250Y 是一款熔融體積流量是8MVR，特性是 脫模性能良好, 中等粘性 ，通用級應用，在Japan實現工業化生產的聚碳酸酯樹脂，長期以來，帝人一直致力於其性能的提高和
瀏覽量：6260
推薦文章
-
PC(聚碳酸酯)HL-4000|三菱工程塑料|物性表參數
三菱工程塑料Iupilon/NOVAREX/XANTAR PC HL-4000是高亮度導光品級;體積熔融指數63厘米3/10分鍾; 易脫模; 注塑成型,三菱工程的聚碳酸酯，在市場上已有好多年曆史, 被廣泛地用於各種工業生產，如運動器械、醫療器械、汽車部件、光學儀器、機械、辦公自動化設備和電子設備，獲得了客戶的廣泛信賴和支持, 三菱工程塑料以自
-
PA66(尼龍66)1402G|Leona(尼胺龍)|旭化成|物性表參數
旭化成Leona(尼胺龍)PA66 1402G是一種增強的強度和剛性，具有良好的抗熱老化性，玻璃纖維含量為33%尼龍66材料，比重是1.39g/cm³，應用於加熱器水箱，燃料噴射器，防滑刹車係統感測器，以及汽車其他機罩下零件。以下是PA66(尼龍66)1402G/Leona(尼胺龍)/旭化成/物性表參數物理性能幹燥調節後的單位製
-
PA6(尼龍6)BKV30GW1/德國朗盛/物性表參數
德國朗盛 LANXESS Durethan PA6 BKV30GW1 是一種加入30%玻璃纖維，注塑，熱老化穩定尼龍6樹脂，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌
-
PC(聚碳酸酯)TC-8001G/韓國樂天化學/物性表參數
韓國樂天化學的(LOTTE Chemical HOPELEX) PC TC-8001G 是一種聚碳酸脂塑料(Polycarbonate)，厚度0.8 mm是防火V-0，不透明的導熱塑膠原料，特性是電絕緣，應用於LED 照明散熱板。 以下是PC(聚碳酸酯)
-
PC(聚碳酸酯)EXL5429/沙伯基礎/物性表參數
Lexan PC EXL5429 是聚碳酸酯(PC)樹脂是一個GF增強，UV穩定，阻燃注射成型共聚物混合。這種介質流樹脂以非氯、非溴化FR試劑為基礎，具有良好的加工性能和提高的釋放性能，具有UL94 V0 @
-
Makrolon(模克隆)FR6002|科思創|PC(聚碳酸酯)物性表參數
科思創Makrolon FR6002 PC 是全球品級; 體積熔融指數MVR (300 C/1.2 kg) 18 cm/10 min;加阻燃劑低粘度PC塑膠原料,PC FR6002主要用於防火產品。 Makrolon FR6002 PC物性表參數PDF文檔下載 以下是科思創Makro
-
POM(聚甲醛樹脂)LM511|旭化成(AsahiKASEI)物性表參數
旭化成(AsahiKASEI)TENAC(鐵耐克)POM LM511具有耐金屬和塑料摩擦和磨損性的聚甲醛樹脂，密度 1.42(g/cm³)，彎曲模量2800(MPa) ，簡支梁缺口衝擊強度7.0(kJ/m²) ，典型用途領域包括工程/工業配件、房屋和汽車行業。TENAC LM511 POM物性表參數PDF文檔下載以下是POM(聚甲醛樹脂)LM511|旭化成(AsahiKASEI)物性表參數物理性能
-
VYDYNE(泛達)奧升德R220|PA66(尼龍66)物性表參數
奧升德VYDYNE PA66 R220是一種40%礦物增強尼龍6,6樹脂，用於提高衝擊強度。它是一種注塑級配方，保留了未加筋PA66固有的加工優勢，同時提高了剛性、強度和耐熱性，Vydyne R220保持尼龍對多種化學品、汽油、油脂和溶劑的典型耐化學性，Vydyne R220樹脂采用獨特的礦物增強尼龍係統，由Ascend Performance Materials開發，以滿
-
Bayblend(拜本蘭)T88GF-30|科思創(PC+SAN合金)物性表參數
科思創 Bayblend PC/SAN T88GF-30是橡膠改性(PC +SAN)混合;10%玻璃纖維增強;維卡軟化點溫度/ B 120 = 134C;優化的熱老化-和uv -穩定性;很好的流;拉伸模量= 10000MPa;良好的耐熱性 PC/ABS是聚碳酸酯和丙烯
-
PC(聚碳酸酯)LUX9130C/沙伯基礎/物性表參數
LEXAN PC LUX9130C 聚碳酸酯(PC)樹脂是一種非填充的、可注射的模數。這種非氯化、非溴化阻燃型PC在1.5毫米、高流動性能和UV穩定的情況下，具有UL-94 V0等級，提供了額外的耐老化性能。Le