PA6(尼龍6)BKV30FN00/德國朗盛/物性表參數

日期：2020-04-14 09:46:19 編輯：科思德塑膠來源：科思德塑膠瀏覽：284

德國朗盛 LANXESS Durethan PA6 BKV30FN00是一種加入30%玻璃纖維，注塑，無鹵阻燃，熱老化穩定尼龍6樹脂，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一係列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
PA6 BKV30FN00

以下是PA6(尼龍6)BKV30FN00/德國朗盛/物性表參數

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.2
	Molding shrinkage, transverse	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.6
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.2
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	11000	6700
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	145	90
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	3.0	6.1
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	65	65
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	60
	Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	<10
	Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	<10
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	55	55
	Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	55
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	<10
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	<10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	10500	6000
	Flexural strength	2 mm/min	MPa	ISO 178-A	225	140
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.1	4.6
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A		128
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	220
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	204
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	218
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	210
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.2
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.8
	Burning behavior UL 94	1.5 mm	Class	UL 94	V-0
	Burning behavior UL 94	0.75 mm	Class	UL 94	V-0
	Burning behavior UL 94-5V	1.5 mm	Class	UL 94	5VA
	Oxygen index	Method A	%	ISO 4589-2	32
	Resistance to heat (ball pressure test)		°C	IEC 60695-10-2	209
	Glow wire test (GWFI)	0.75 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	1.5 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	3.0 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWIT)	0.75 mm	°C	IEC 60695-2-13	775
	Glow wire test (GWIT)	1.5 mm	°C	IEC 60695-2-13	775
	Glow wire test (GWIT)	3.0 mm	°C	IEC 60695-2-13	800
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	4.4	10.2
	Relative permittivity	1 MHz	-	IEC 60250	3.9	4.5
	Volume resistivity		Ohm·m	IEC 60093	4E+13	2E+10
	Electric strength	1 mm	kV/mm	IEC 60243-1	36	32
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	600
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	5
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	1.5
	Density		kg/m³	ISO 1183	1443
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	260
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.07
	Melt temperature (Tmin - Tmax)		°C	-	250-270
	Mold temperature		°C	-	80-100

德國朗盛LANXESS Durethan PA6 BKV30FN00具有高抗震及抗裂性能，具體指標與材料的等級與含水量有關。彈性體改性的材料即使在低含水量及低溫下也具有良好的韌性,硬度高，尤其對於玻纖增強級別產品；拉伸模量：1,300 到 15,700 MPa (取決於含水量),良好的機械性能及阻尼吸聲效應、低摩擦力、急速運行能力好，氣體阻隔性能好（薄膜級）.

密度	1.01~1.23	模具溫度	80.0 到 100°C
加工（熔體）溫度	260 到 270°C	注射壓力	230 到 250°C
預熱	溫度/°C	130°C	工藝參數	注射時間	20~90
時間/h	4.0hr	高壓時間	0~5
料桶溫度/°C	後段	193 到 238°C	冷卻時間	20~90
中段	210 到 249°C	總周期	220 到 260°C
前段	221 到 254°C	螺杆轉數	30 到 60rpm
噴嘴溫度	232 到 274°C	使用注射機類型	螺杆式