德國朗盛 LANXESS Durethan PA6 B30SFN40是一種無增強，注塑，阻燃尼龍6樹脂,根據特定的材料及所需等級，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一係列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
生產商：LANXESS(德國朗盛)、品名：Durethan
PA6(尼龍6)B30SFN40/德國朗盛/物性表參數

These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.

Property		Test Condition	Unit	Standard	guide value
					d.a.m.	cond.
Rheological properties
	Molding shrinkage, parallel	150x105x3; 260 °C / MT 80 °C; 500 bar	%	acc. ISO 2577	0.9
	Molding shrinkage, transverse	150x105x3; 260 °C / MT 80 °C; 500 bar	%	acc. ISO 2577	0.9
	Post- shrinkage, parallel	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.2
	Post- shrinkage, transverse	150x105x3; 120 °C; 4 h	%	acc. ISO 2577	0.2
	Molding shrinkage, parallel	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.9
	Molding shrinkage, transverse	60x60x2; 260 °C / MT 80 °C; 600 bar	%	ISO 294-4	0.9
	Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.3
	Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.3
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	3400	1100
	Yield stress	50 mm/min	MPa	ISO 527-1,-2	90	45
	Yield strain	50 mm/min	%	ISO 527-1,-2	4.0	22.5
	Nominal strain at break	50 mm/min	%	ISO 527-1,-2	9.6	265
	Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	60	65
	Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	15.5	293
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	N	N
	Izod impact strength	23 °C	kJ/m²	ISO 180-1U	N	N
	Izod notched impact strength	23 °C	kJ/m²	ISO 180-1A	< 10
	Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	< 10
	Flexural modulus	2 mm/min	MPa	ISO 178-A	3000	900
	Flexural strength	2 mm/min	MPa	ISO 178-A	120	35
	Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	5.9	8.1
	Flexural stress at 3.5 % strain	2 mm/min	MPa	ISO 178-A	100	26
	Ball indentation hardness		N/mm²	ISO 2039-1	135
Thermal properties
	Melting temperature	10 °C/min	°C	ISO 11357-1,-3	222
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	66
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	166
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.9
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.8
	Burning behavior UL 94	1.5 mm	Class	UL 94	V-2
	Burning behavior UL 94	0.4 mm	Class	UL 94	V-2
	Oxygen index	Method A	%	ISO 4589-2	28
	Glow wire test (GWFI)	0.4 mm	°C	IEC 60695-2-12	900
	Glow wire test (GWFI)	0.75 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	1.5 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWFI)	3.0 mm	°C	IEC 60695-2-12	960
	Glow wire test (GWIT)	0.4 mm	°C	IEC 60695-2-13	930
	Glow wire test (GWIT)	0.75 mm	°C	IEC 60695-2-13	875
	Glow wire test (GWIT)	1.5 mm	°C	IEC 60695-2-13	850
	Glow wire test (GWIT)	3.0 mm	°C	IEC 60695-2-13	750
Electrical properties (23 °C/50 % r. h.)
	Volume resistivity		Ohm·m	IEC 60093	4E+13
	Surface resistivity		Ohm	IEC 60093	3E+15
	Electric strength	1 mm	kV/mm	IEC 60243-1	29
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	600
Other properties (23 °C)
	Water absorption (Saturation value)	Water at 23 °C	%	ISO 62	10.0
	Water absorption (Equilibrium value)	23 °C; 50 % RH	%	ISO 62	3.0
	Density		kg/m³	ISO 1183	1140
	Bulk density		kg/m³	ISO 60	700
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	260
	Injection molding-Mold temperature		°C	ISO 294	80
Processing recommendations
	Drying temperature dry air dryer		°C	-	80
	Drying time dry air dryer		h	-	2-6
	Residual moisture content		%	Acc. to Karl Fischer	0.03-0.07
	Melt temperature (Tmin - Tmax)		°C	-	250-270
	Mold temperature		°C	-	80-100